To evaluate the effect of different enamel conditioning procedures on the shear bond strength of new metal bracket on previously debonded tooth surface - An in-vitro study.

Dr navdeep kaur,
Dr Puja Khanna,
Dr. Sunny Mittal,
Dr. Harshika Gupta,
Dr. Nishtha Arora,
Dr SUMIT Chhaora,
dr. Neha Kaswan

Abstract

Objective: To evaluate the efficacy of different enamel conditioning methods while bonding a new bracket on a previously de-bonded site, assess the difference in shear bond strength and ARI score if any. Materials and methods: 125 human extracted premolars were selected. 250 premolar brackets were procured. 125 brackets were bonded on the buccal surface of the premolars using different enamel conditioning methods. (Bonding sequence I) and was followed by debonding using Instron Universal testing machine (Debonding procedure I). The remaining 125 brackets were bonded (Bonding sequence II) on the same teeth after removal of residual adhesive. Bonding sequence II was followed by debonding (Debonding procedure II), shear bond strength calculation and ARI score calculation. Results: There was a significant difference in SBS between 5 groups after initial debonding. SEP group (group 4) showed the highest SBS followed by acid etching groups (groups 3, 2, and 1). Sandblasting group (group 5) had the least shear bond strength value. After the second debonding, SBS was found to be highest in Group 3 {37% o-phosphoric acid (Bonding I) sandblasting (Bonding II)} followed by group 4 {SEP (Bonding I and Bonding II)}, group 2 {acid etching (Bonding I) SEP (Bonding II)}, and group 1 (acid etching in both bonding sequence). Group 5 (sandblasting in both sequences) had the least SBS. Non significant differernces were found in ARI score of the five groups. Conclusion: Self-etching primer group had highest SBS and sandblasting group had least SBS after first debond. The SBS of new brackets after two debonding procedures significantly decreased but was still found to be above the required bond strength. SEP and sandblasting can be used as a substitute to acid etching technique in second time bonding of brackets as these groups had higher SBS after second debond.